PA6 BM 25 FN20 DUS013 000000德國(guó)朗盛Durethan 25%礦物無(wú)鹵阻燃尼龍6塑料（18024445500）

PA 6, 25 % mineral, injection molding, halogen free flame retardant, optimized for laser marking (1064nm)



ISO Shortname: ISO 1874-PA 6, GFHR, 14-060, MD25; ISO 1043-PA MD FR (30)

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.9　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.9　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.2　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.2　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 5700 2100
C Yield stress 50 mm/min MPa ISO 527-1,-2 80 30
C Yield strain 50 mm/min % ISO 527-1,-2 3.0 8.0
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 80 30
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 7.0
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 38 135
Izod impact strength 23 °C kJ/m² ISO 180-1U 30 100
Izod notched impact strength 23 °C kJ/m² ISO 180-1A <10 <10
Flexural modulus 2 mm/min MPa ISO 178-A 5500 2000
Flexural strength 2 mm/min MPa ISO 178-A 130 50
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3.3 6.8
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 130 43